UNS | AISI / ASTM | DIN / EN | |||
S31803/S32205 | S31803 | 1.4462 | |||
Konpozisyon chimik: | |||||
% | C | Mn | P | S | Si |
Min | |||||
Maks | 0.03 | 2 | 0.03 | 0.02 | 1 |
Ni | Cr | Mo | N | ||
Min | 4.5 | 21 | 2.5 | 0.08 | |
Maks | 6.5 | 23 | 3.5 | 0.2 | |
Pèfòmans fizik: | |||||
Tretman Chalè | T*S | Y*S | El | Dite | |
Mpa | Mpa | % | HB | ||
1020-1100 | 620 | 450 | 25 | ≤290 | |
Done | |||||
UNS | AISI / ASTM | DIN / EN | |||
UNS S32750 | SAF 2507 | 1.441 | |||
Konpozisyon chimik: | |||||
% | C | Mn | P | S | Si |
Min | |||||
Maks | 0.03 | 1.2 | 0.035 | 0.02 | 0.8 |
Ni | Cr | Mo | N | ||
Min | 6 | 24 | 3 | 0.24 | |
Maks | 8 | 26 | 5 | 0.32 | |
Pèfòmans fizik: | |||||
Tretman Chalè | T*S | Y*S | El | Dite | |
Mpa | Mpa | % | HB | ||
1025-1125 | 800 | 550 | 15 | ≤310 | |
347 Duplex Nerjaveèi asye ba se korozyon trè rezistan, travay alyaj Hardenable. 347 Duplex Nerjaveèi asye Bar gen nivo relativman wo nan CHROMIUM (ant 18% ak 28%) ak ba kantite modere nan nikèl (ant 1.5% ak 8%). Rezistans nan korozyon segondè, epi ekselan pwopriyete mekanik nan 347 Duplex Nerjaveèi asye Bar ka atribiye nan konpozisyon chimik yo ak mikrostruktur balanse (duplex) nan pousantaj apeprè egal volim nan ferit ak ostenit.
1. Creole pake ekspòte.
2. Original pake oswa pake net.
3. Dapre kliyan' bezwen.
4. anbake in10-35 jou apre peman.